35536. Steel 27mncrb5-2 1.7182 Pipe&Tube for General Engineering 
[Jul 29, 2024]
[Jul 29, 2024] 1.[ 27MnCrB5-2 1.7182 pipe&tube ] introduction: Standard: EN 10083-3: 2006 Steels for quenching and tempering. Technical delivery conditions for alloy steels Equivalent grades of steel 38MnB5 ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35537. Structural Steel 14nicr14 1.5752 Ecn35 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Structural steel 14NiCr14 1.5752 ECN35 bar& rod] Introduction: Chemical composition(mass fraction)(wt.%) of the 14NiCr14 C ≤ Si ≤ Mn ≤ P ≤ S ≤ Cr Ni 0.14-0.20 0.40 ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35538. Structural Steel 16mncrs5 1.7139 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Structural steel 16MnCrS5 1.7139 EC80 bar& rod] Introduction: Heat treated : 1789°C - 1751°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35539. Constructional Steel 20mocr4 1.7321 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 20MoCr4 1.7321 bar& rod] Introduction: Heat treated : 1627°C - 1119°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35540. Constructional Steel 34cralmo5 1.8507 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 34CrAlMo5 1.8507 bar& rod] Introduction: Heat treated : 1474°C - 1676°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35541. Constructional Steel 31crmo12 1.8515 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 31CrMo12 1.8515 bar& rod] Introduction: Heat treated : 1554°C - 1668°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35542. Constructional Steel 9s20 1.0711 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 9S20 1.0711 bar& rod] Introduction: Heat treated : 1669°C - 1636°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35543. Constructional Steel 15s20 1.0723 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 15S20 1.0723 bar& rod] Introduction: Heat treated : 1762°C - 1465°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35544. Constructional Steel C22 1.0402 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel C22 1.0402 bar& rod] Introduction: Heat treated : 1591°C - 1258°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35545. Constructional Steel 20mn5 1.1133 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 20Mn5 1.1133 bar& rod] Introduction: Heat treated : 1338°C - 1676°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35546. Constructional Steel Cm45 1.1201 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel Cm45 1.1201 bar& rod] Introduction: Heat treated : 1562°C - 1368°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35547. Constructional Steel X120mn12 1.3401 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel X120Mn12 1.3401 bar& rod] Introduction: Heat treated : 1654°C - 1456°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35548. Constructional Steel 46mnsi4 1.5121 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 46MnSi4 1.5121 bar& rod] Introduction: Heat treated : 1735°C - 1114°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35549. Constructional Steel 42mnv7 1.5223 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 42MnV7 1.5223 bar& rod] Introduction: Heat treated : 1138°C - 1545°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
35550. Constructional Steel 37cr4 1.7034 Rod & Bar for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 37Cr4 1.7034 bar& rod] Introduction: Heat treated : 1562°C - 1164°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.